Effect of Graphite Coating on the Corrosion Resistance of Uranium Surface

摘要: 为了提高铀的抗氧化腐蚀能力,利用石墨的粘附特性,在铀表面涂覆一层石墨,并进行真空热处理,在100 ℃条件下对热处理后的样品进行氧化腐蚀试验。结果表明,在测量腐蚀增重时间内,无论是初始氧化腐蚀还是长时间氧化腐蚀,经过真空热处理后的石墨层均能够起到对铀表面的保护作用。对不同热处理工艺参数对抗腐蚀性的影响进行了探讨,认为涂覆石墨层的铀表面经真空热处理后,表面膜层所发生的变化是提高铀表面抗腐蚀性的主要原因。
- 铀 /
- 石墨 /
- 真空热处理 /
- 腐蚀
Abstract: Influence of vacuum heat-treatment on the corrosion resistance of uranium surface overlaid with graphite at 100 ℃ is studied. The results show that the graphite coat after vacuum heat treatment can protect the uranium surface. The corrosion resistance of uranium surface overlaid with graphite depends on the heat treatment time and temperature. It can be expected that the reaction product of uranium and graphite may be beneficial to improving the corrosion resistance for uranium surface.
- uranium /
- graphite /
- vacuum heat treatment /
- corrosion resistance

[1]	ArkushR,MintzM H,ShamirN.Passivation ofUraniumTowardsAirCorrosion byN+2 andC+IonImplanation[J].J NuclMater,2000,281:182~190.
[2]	王小英,刘天伟,勾引宁,等贫铀表面碳氧离子注/渗及其抗蚀性能研究[J]表面技术,2002,31(1):12~15
[3]	杨江荣,邹觉生,蒋春丽,等CO处理对铀在40℃和70℃潮湿空气中抗蚀性能的影响[J]核化学与放射化学,2002,24(1):34~37
[4]	张广丰,杨维才,汪小琳,等超临界CO2后的金属铀表面氧化腐蚀和电化学腐蚀实验研究[J]原子能科学技术,2003,37(3):233~236
[5]	刘柯钊,赖新春,愈勇,等金属铀表面含氧碳化物的组成与性质[R]中国核科技报告:CNIC 01383/SMI 0016,北京:原子能出版社,1999
[6]	黄桂芳,周灵平,李绍禄,等离子束沉积类金刚石膜对钢在NaCl溶液中耐蚀性能的影响[J]材料保护,2000,33(6):35~36
[7]	李士贤,姚建,林定浩石墨[M]北京:化学工业出版社,199115~17