TEST OF~(134) Cs, ~(85,89) Sr LEACHING RATE IN A RESEMBLE VITRIFIABLE CEMENT WASTE FORM[J]. Journal of Nuclear and Radiochemistry, 2003, 25(3): 134-134.
    Citation: TEST OF~(134) Cs, ~(85,89) Sr LEACHING RATE IN A RESEMBLE VITRIFIABLE CEMENT WASTE FORM[J]. Journal of Nuclear and Radiochemistry, 2003, 25(3): 134-134.

    TEST OF~(134) Cs, ~(85,89) Sr LEACHING RATE IN A RESEMBLE VITRIFIABLE CEMENT WASTE FORM

    • A novel material——resemble vitrifiable cement for conditioning low and mediate level radioactive waste has been developed. Waste form has been characterized for their physical and chemical performance, phase composition. The cement formulation has been patented. In this experiment the cement is mixed with simulated wastes spiked with 134 Cs and 85,89 Sr by 5 min at least. The Ratio of the waste to the cement is 0.45~0.55. The mixture is packed into cylindrical molds which has the same dimension of diameter and height. The grouts are cured for a period of 28 d in a room temperature curing chamber at an atmospheric pressure. The cured waste form is then completely immersed into deionized water. According to standard GB7023-86, leaching rate of 134 Cs and 85,89 Sr are measured. The result shows that the leaching rate of the species 134 Cs and 85,89 Sr is to be on the order 10 -4 and 10 -5 on the 42 d immersion, respectively and is better than that of commercial cement.
    • loading

    Catalog

      Turn off MathJax
      Article Contents

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return